Abstract Dental alloys are widely used in fabrication of removable partial dentures, particularly as a dental framework. The present study aimed at studying the effect of the commercial mouthwashes on the corrosion behavior of the Co−Cr dental casting alloy. Corrosion behavior was investigated in alcohol-free and alcohol-containing mouthwashes added to artificial saliva solutions at room temperature by electrochemical tests recorded the open circuit potential (OCP) and current density, after the surface analysis of the samples was performed. During the early 250s, the OCP values showed significant changes, with the exception of one test group containing alcohol, where potential decreased continuously during the test, which also recorded the highest current density, different from the other groups. It was observed that the presence of alcohol increased the current density and the corrosion process in this alloy and the mouthwashes had more aggressive action in specimens submitted to solutions with alcohol in the composition.

Objective The aim of this study was to evaluate the electrochemical behavior of a cobalt-chromium (Co-Cr) dental alloy after immersion in denture cleansers. Method: Twenty-four specimens (Ø13x2mm) of Co-Cr were produced and divided into three groups (n=8) according to their experimental condition. The group 1 (control group) was composed only of distilled water, group 2 received a hygienic tablet (Corega Tabs™) at the moment that electrochemical test started, while the group 3 received the hygienic tablet (Corega Tabs™) 1h after immersion. The electrochemical tests recorded the open circuit potential (OCP) and current density (icorr). The surfaces of specimens were examined using a SEM. Data were statistically analyzed using analysis of variance (ANOVA) and Duncan test’ multiple comparisons post hoc analysis (α=0.05). Results: The values of OCP and icorr revealed statistically differences between the groups. The highest results were recorded for group 2 (-26.87±48.48mV; 0.29±0.22μA), which were similar to group 3 (-47.37±35.36mV; 0.26±0.10μA), and these values were difference to group 1 (-314.87±24.22mV; 0.50±0.17μA). SEM image show high corrosion with Corega Tabs™. Conclusion: The immersion in denture cleanser solution was not detrimental to the Co-Cr dental alloy and presented a lower tendency to corrosion process development than the control group.

Resumo Neste estudo foi avaliado desajuste vertical, a passividade e a distribuição de tensões após o aperto dos parafusos de diferentes próteses. Dois implantes foram usados para simular a reabilitação do espaço edêntulo da mandíbula do segundo pré-molar ao segundo molar. Quarenta próteses dentárias fixas parafusadas de três elementos com cantilever distal foram confeccionadas e separadas em quatro grupos de acordo com o método de obtenção da infraestrutura (n = 10): G1 = fundição convencional estrutura monobloco, G2 = fundição convencional seccionada e soldagem a laser, G3 = fundição convencional seccionada e soldagem com gás inerte de tungstênio (TIG) e G4 = infraestrutura obtida pelo sistema CAD / CAM (computer-aided design/computer-aided manufacturing). Os desajustes verticais com ambos os parafusos apertados e os desajustes relativos à avaliação de passividade com um parafuso apertado foram medidos com microscópio comparador óptico. Os dados foram submetidos ao teste de Shapiro-Wilk para comparação com ANOVA seguida de ajuste de Tukey com Bonferroni (α = 0,05). A análise qualitativa da distribuição de tensões foi realizada pelo método fotoelástico. G2 (24 μm) e G3 (27 μm) apresentaram valores significativamente maiores que G4 (10 μm) (p = 0,006) de desajuste vertical (ambos os parafusos apertados). Os valores de desajustes nos G1 (64 μm) e G3 (61 μm), do lado não apertado, foram significativamente maiores que no G4 (32 μm) (p = 0,009). G1 apresentou maior tensão entre os implantes na análise fotoelástica e G4 apresentou menor tensão. O método CAD/CAM resultou em menor desajuste, maior passividade e melhor distribuição de tensões no osso.

Abstract This study evaluated the vertical misfit, passivity, and stress distribution after tightening the screws of different prosthesis. Two implants were used to simulate the rehabilitation of partially edentulous mandible space from the second premolar to the second molar. 40 three-element screw-retained fixed dental prosthesis with distal cantilever were fabricated and divided into four groups according to the method of production of framework (n = 10): G1 = conventional casting one-piece framework, G2 = conventional casting sectioned and laser welding, G3 = conventional casting sectioned and tungsten inert gas (TIG) welding and G4 = framework obtained by CAD/CAM (computer-aided design/computer-aided manufacturing) system. The vertical misfits (both screws tightened) and the passive fit (one screw tightened) were measured under a comparator optical microscope. The data was submitted to Shapiro-Wilk test to enable comparison with ANOVA followed by Tukey with Bonferroni adjust (α = .05). The qualitative analysis of the stress distribution was performed by the photoelastic method. The vertical misfit (both screws tightened) of the G2 (24 μm) and G3 (27 μm) were significantly higher than G4 (10 μm) (p = 0,006). The passive fit (for the non-tightened) of the G1(64 μm) and G3 (61 μm) were significantly higher than the G4 (32 μm) (p=0,009). G1 showed high stress between the implants in the photoelastic analysis and G4 presented lower stress. In conclusion, CAD/CAM method results in less vertical misfit, more passivity, and consequently better stress distribution to the bone.

Resumo Esta pesquisa avaliou a influência dos cimentos temporários (contendo eugenol [CE]ou livre de eugenol[LE]) na resistência à tração de copingsde Ni-Cr fixados com cimento resinoso auto-adesivo sobre substrato coronário metálico. Trinta e seis coroas provisórias foram divididas em 4 grupos (n=9) de acordo com os cimentos temporários: Provy, Dentsply (contendo eugenol), Temp Cem, Vigodent (contendo eugenol), RelyXTemp NE, 3M ESPE (livre de eugenol) andTemp Bond NE, KerrCorp (livre de eugenol). Após 24 h da cimentação temporária, testes de resistência à tração foram realizados em uma máquina universal de ensaios, com velocidade de 0,5 mm/min. e célula de carga de 1kN (100 kgf). Em seguida, os núcleos metálicos fundidos foram limpos por meio de raspagem com cureta ejatos de ar. Trinta e seis copings de Ni-Cr foram cimentados sobre os núcleos metálicos com cimento resinoso auto-adesivo (RelyX U200, 3M ESPE). Testes de resistência à tração foram novamente realizados. Na cimentação provisória, Temp Bond NE (12,91±2,54) e Temp Cem (12,22±2,96) apresentaram os maiores valores de resistência à tração e foram estatisticamente semelhantes entre si (p>0,05). Diferença estatisticamente significante (p<0.05) foi observada apenas entre Provy (164,44±31,23) e Temp Bond NE (88,48±21,83)após cimentação dos copingsdeNi-Cr com cimento resinoso auto-adesivo. Além disso, Temp Cem (120,68±48,27) e RelyX Temp NE (103,04±26,09) mostraram valores intermediários de resistência à tração. Em conclusão, o cimento temporário contendo eugenol, Proxy, foi associado com a mais alta resistência de união do cimento resinoso, quando os copingsde Ni-Cr foram cimentados sobre os núcleos metálicos fundidos. Entretanto, o eugenol não pode ser considerado como um fator determinante no aumento da resistência de união, já que outros cimentos testados (1 contendo eugenol e 2 livres de eugenol) foram semelhantes.

This research evaluated the influence of temporary cements (eugenol-containing [EC] or eugenol-free [EF]) on the tensile strength of Ni-Cr copings fixed with self-adhesive resin cement to the metal coronal substrate. Thirty-six temporary crowns were divided into 4 groups (n=9) according to the temporary cements: Provy, Dentsply (eugenol-containing), Temp Cem, Vigodent (eugenol-containing), RelyX Temp NE, 3M ESPE (eugenol-free) and Temp Bond NE, Kerr Corp (eugenol-free). After 24 h of temporary cementation, tensile strength tests were performed in a universal testing machine at a crosshead speed of 0.5 mm/min and 1 kN (100 kgf) load cell. Afterwards, the cast metal cores were cleaned by scraping with curettes and air jet. Thirty-six Ni-Cr copings were cemented to the cast metal cores with self-adhesive resin cement (RelyX U200, 3M ESPE). Tensile strength tests were performed again. In the temporary cementation, Temp Bond NE (12.91±2.54) and Temp Cem (12.22±2.96) presented the highest values of tensile strength and were statistically similar to each other (p>0.05). Statistically significant difference (p<0.05) was observed only between Provy (164.44±31.23) and Temp Bond NE (88.48±21.83) after cementation of Ni-Cr copings with self-adhesive resin cement. In addition, Temp Cem (120.68±48.27) and RelyX Temp NE (103.04±26.09) showed intermediate tensile strength values. In conclusion, the Provy eugenol-containing temporary cement was associated with the highest bond strength among the resin cements when Ni-Cr copings were cemented to cast metal cores. However, the eugenol cannot be considered a determining factor in increased bond strength, since the other tested cements (1 eugenol-containing and 2 eugenol-free) were similar.

OBJECTIVE: This study aimed to evaluate the importance of a distal proximal contact on the load transfer to the posterior region of the mandible by non-splinted adjacent implant-supported crowns using photoelastic stress analysis. MATERIAL AND METHODS: A rectangular model (68x30x15 mm) was made of polymethylmethacrylate resin to simulate half of the mandibular arch. One model was completed with resin replicas representing the first premolar and second molar and with two 3.75 mm dia.x11 mm internal hexagon threaded implants replacing the second premolar and first molar. The other model was manufactured in the same way but without the second molar. Both models were duplicated using photoelastic resin. The roots of the teeth replicas were covered with a layer of polyether impression material to simulate the periodontal ligament. Two different vertical loads were applied to the crowns as follows: 1 - single static point load alternately applied to the crowns replacing the second premolar and first molar (50 N); 2 - simultaneous static point loads applied to both of the crowns replacing the second premolar and first molar (100 N). The resulting isochromatic fringe pattern in the photoelastic model was monitored and photographed. RESULTS: All loading conditions studied showed that the presence of the second molar has changed the load transmission and the pattern of stresses. CONCLUSION: Results showed that the presence of a second molar proximal contact can help minimize the stresses around the implants.

AIM: To explore the biomechanical effects of the different implantation bone levels of Morse taper implants, employing a finite element analysis (FEA). METHODS: Dental implants (TitamaxCM) with 4x13 mm and 4x11 mm, and their respective abutments with 3.5 mm height, simulating a screwed premolar metal-ceramic crown, had their design performed using the software AnsysWorkbench 10.0. They were positioned in bone blocks, covered by 2.5 mm thickness of mucosa. The cortical bone was designed with 1.5 mm thickness and the trabecular bone completed the bone block. Four groups were formed: group 11CBL (11 mm implant length on cortical bone level), group 11TBL (11 mm implant length on trabecular bone level), group 13CBL (13mm implant length on cortical bone level) and group 13TBL (13 mm implant length on trabecular bone level). Oblique 200 N loads were applied. Von Mises equivalent stresses in cortical and trabecular bones were evaluated with the same design program. RESULTS: The results were shown qualitatively and quantitatively by standard scales for each type of bone. By the results obtained, it can be suggested that positioning the implant completely in trabecular bone brings harm with respect to the generated stresses. Its implantation in the cortical bone has advantages with respect to better anchoring and locking, reflecting a better dissipation of the stresses along the implant/bone interfaces. In addition, the search for anchoring the implant in its apical region in cortical bone is of great value to improve stabilization and consequently better stress distribution. CONCLUSIONS: The implant position slightly below the bone in relation to the bone crest brings advantages as the best long-term predictability with respect to the expected neck bone loss.

Os efeitos do fluoreto, o qual está presente em diferentes produtos de higiene oral, necessita de maiores investigações, pois pouco se sabe sobre seus efeitos na superfície do titânio, o qual possui amplo uso na implantodontia. Este estudo objetivou avaliar a superfície do titânio comercialmente puro (cpTi) após exposição a diferentes concentrações de fluoreto de sódio (NaF). A hipótese testada neste estudo foi que diferentes concentrações de NaF aplicadas em diferentes intervalos de tempo seriam capazes de afetar diferentemente a superfície do titânio. Os tratamentos realizados foram: GA (controle): imersão em água destilada; GB: imersão diária por 3 min em NaF a 0,05%; GC: imersão diária por 3 min em NaF a 0,2%; GD: imersão quinzenal por 3 min em NaF a 0,05%; e GE: imersão quinzenal por 3 min em NaF a 0,2%. O tempo do experimento foi de 60 dias. A análise da rugosidade foi efetuada inicialmente e a cada 15 dias. Após 60 dias foi realizada análise de corrosão e polarização anódica. As amostras foram analisadas em MEV. Os dados de rugosidade foram analisados por ANOVA e não houve diferença estatisticamente significante entre grupos e entre tempos. Os dados de corrosão (i corr) foram analisados pelo teste de Mann-Whitney e foram encontradas diferenças significantes entre GA e GC, GC e GB, GC e GD, GC e GE. A MEV evidenciou que a superfície do titânio exposto ao NaF apresentou corrosão variando de acordo com a concentração. Com base nos dados encontrados conclui-se que o uso de solução NaF a 0,05% em cpTi é seguro, enquanto a solução NaF 0,2% para uso diário deve ser cuidadosamente avaliada.

The effects of fluoride, which is present in different oral hygiene products, deserve more investigation because little is known about their impact on the surface of titanium, which is largely used in Implantology. This study evaluated the surface of commercially pure titanium (cpTi) after exposure to different concentrations of sodium fluoride (NaF). The hypothesis tested in this study was that different concentrations of NaF applied at different time intervals can affect the titanium surface in different ways. The treatments resulted in the following groups: GA (control): immersion in distilled water; GB: immersion in 0.05% NaF for 3 min daily; GC: immersion in 0.2% NaF for 3 min daily; GD: immersion in 0.05% NaF for 3 min every 2 weeks; and GE: immersion in 0.2% NaF for 3 min every 2 weeks. The experiment lasted 60 days. Roughness was measured initially and every 15 days subsequently up to 60 days. After 60 days, corrosion analysis and anodic polarization were done. The samples were examined by scanning electron microscopy (SEM). The roughness data were analyzed by ANOVA and there was no significant difference among groups and among time intervals. The corrosion data (i corr) were analyzed by the Mann-Whitney test, and significant differences were found between GA and GC, GB and GC, GC and GD, GC and GE. SEM micrographs showed that the titanium surface exposed to NaF presented corrosion that varied with the different concentrations. This study suggests that the use of 0.05% NaF solution on cpTi is safe, whereas the 0.2% NaF solution should be carefully evaluated with regard to its daily use.

O objetivo deste estudo foi avaliar a perda do torque inicial, quando usados novos parafusos de pilares e após sucessivos apertos. Quatro infra-estruturas (IE), utilizando pilares calcináveis tipo UCLA, foram fundidas em liga de cobalto-cromo, onde novos parafusos de pilares foram utilizados (G1) em um primeiro momento. Posteriormente os mesmos parafusos de pilares foram utilizados em um segundo momento (G2), e depois por mais duas vezes (G3). Os valores de torque e detorque aplicados foram mensurados a partir de um torquímetro digital para obtenção dos valores de perda do torque inicial (%). Os dados foram coletados e submetidos à análise de variância e teste de Tukey (p<0,05). Foram observadas diferenças estatisticamente significantes entre os grupos G1 (50,71% ± 11,36) and G2 (24,01% ± 3,33) (p=0,000) and the groups G1 (50,71% ± 11,36) and G3 (25,60% ± 4,64) (p=0,000). Os maiores valores foram encontrados para o grupo G1. Não houve diferença estaticamente significante entre os grupos G2 e G3 (p=0,774). Dentro das limitações deste estudo, pôde-se observar que a porcentagem de perda de torque inicial foi menor quando os parafusos já haviam sofrido a aplicação do primeiro torque, se mantendo estáveis após os demais torques.

This study evaluated the loss of the torque applied after use of new screws and after successive tightening. Four infrastructures (IE), using UCLA castable abutment type, were cast in cobalt-chromium alloy and new abutment screws (G1) were used in a first moment. Subsequently, the same abutment screws were used a second time (G2) and more than two times (G3). The values of the torques applied and detorques were measured with a digital torque wrench to obtain the values of initial tightening loss (%). Data were analyzed by ANOVA and Tukey's test (?=0.05). Significant differences were observed between the G1 (50.71% ± 11.36) and G2 (24.01% ± 3.33) (p=0.000) and between G1 (50.71% ± 11.36) and G3 (25.60% ± 4.64) (p=0.000). There was no significant difference between G2 and G3 (p=0.774). Within the limitations of the study, it may be concluded that the percentage of the initial torque loss is lower when screws that already suffered the application of an initial torque were used, remaining stable after application of successive torques.

The interest in using titanium to fabricate removable partial denture (RPD) frameworks has increased, but there are few studies evaluating the effects of casting methods on clasp behavior. OBJECTIVE: This study compared the occurrence of porosities and the retentive force of commercially pure titanium (CP Ti) and cobalt-chromium (Co-Cr) removable partial denture circumferential clasps cast by induction/centrifugation and plasma/vacuum-pressure. MATERIAL AND METHODS: 72 frameworks were cast from CP Ti (n=36) and Co-Cr alloy (n=36; control group). For each material, 18 frameworks were casted by electromagnetic induction and injected by centrifugation, whereas the other 18 were casted by plasma and injected by vacuum-pressure. For each casting method, three subgroups (n=6) were formed: 0.25 mm, 0.50 mm, and 0.75 mm undercuts. The specimens were radiographed and subjected to an insertion/removal test simulating 5 years of framework use. Data were analyzed by ANOVA and Tukey's to compare materials and cast methods (α=0.05). RESULTS: Three of 18 specimens of the induction/centrifugation group and 9 of 18 specimens of plasma/vacuum-pressure cast presented porosities, but only 1 and 7 specimens, respectively, were rejected for simulation test. For Co-Cr alloy, no defects were found. Comparing the casting methods, statistically significant differences (p<0.05) were observed only for the Co-Cr alloy with 0.25 mm and 0.50 mm undercuts. Significant differences were found for the 0.25 mm and 0.75 mm undercuts dependent on the material used. For the 0.50 mm undercut, significant differences were found when the materials were induction casted. CONCLUSION: Although both casting methods produced satisfactory CP Ti RPD frameworks, the occurrence of porosities was greater in the plasma/vacuum-pressure than in the induction/centrifugation method, the latter resulting in higher clasp rigidity, generating higher retention force values.

Este estudo tem como objetivo comparar o ajuste vertical e a passividade de infraestruturas em monobloco confeccionadas em 3 diferentes materiais: titânio comercialmente puro (Ti cp - G1), cobalto-cromo (Co-Cr - G2) e níquel-cromo-titânio (Ni-Cr-Ti - G3). Quinze infraestruturas foram obtidas simulando barras para próteses fixas em um modelo com 5 implantes. O ajuste vertical e a passividade da interface da infraestrutura foram medidos usando um microscópio óptico (30×). Os dados foram analisados estatisticamente por meio da ANOVA e teste LSD (α=0,05). A média dos valores e o desvio-padrão da passividade e do ajuste vertical estão apresentados respectivamente: Ti cp [472,49 (109,88) μm e 29,9 (13,24) μm], Co-Cr [584,84 (120,20) μm e 27,05 (10,30) μm], Ni-Cr-Ti [462,70 (179,18) μm e 24,95 (11,14) μm]. Para o desajuste vertical, não houve diferença significante entre o Ti cp e as ligas Co-Cr e Ni-Cr-Ti (p=0,285). Para passividade, não houve diferença significante entre Ti cp e Ni-Cr-Ti (p=0,844), mas ambos foram estatisticamente diferentes do Co-Cr (p=0,028 e p=0,035, respectivamente), o qual apresentou os piores resultados. Pode-se concluir que os materiais utilizados para confecção das infraestruturas não influenciaram o ajuste vertical e que infraestruturas fundidas em monobloco resultaram em inadequados ajustes passivos. A liga de Co-Cr apresentou os piores resultados para a passividade.

This study compared vertical and passive fit of one-piece cast frameworks made with 3 different materials: commercially pure titanium (CP Ti - G1), cobalt-chromium alloy (Co-Cr - G2) and nickel-chromium-titanium alloy (Ni-Cr-Ti - G3). Fifteen frameworks were obtained simulating bars for fixed prosthesis in a model with 5 implants. The passive and vertical fit of the framework interface was measured using an optical microscope at ×30 magnification. Data were statistically analyzed by ANOVA and LSD tests (α=0.05). Mean and standard deviation values for passive fit and vertical fit were, respectively: G1 [472.49 (109.88) µm and 29.9 (13.24) µm], G2 [584.84 (120.20) µm and 27.05 (10.30) µm], and G3 [462.70 (179.18) µm and 24.95 (11.14) µm]. For vertical fit, there were no significant differences among G1, G2 and G3 (p=0.285). There were no significant differences for passive fit between G1 and G3 (p=0.844), but both differed significantly from G2 (p=0.028 and p=0.035, respectively), which showed the highest misfit values. It may be concluded that the vertical fit of frameworks was not affected by the tested materials, and that one-piece cast frameworks resulted in inadequate passive fit. The Co-Cr alloy presented the worst values for passive fit.

Cell culture system has been used to evaluate alloy cytotoxicity under different environments, testing the extracts, but the effect of temperature variation on the cytotoxicity of dental alloys has not been analyzed. OBJECTIVE: The aim of the present study was to investigate if temperature variation could affect dental alloy cytotoxicity, testing alloy extracts in an epithelial cell culture system. MATERIAL AND METHODS: Discs of Ni-Cr, Co-Cr-Mo, Ni-Cr-Ti, Ti-6Al-4V and commercially pure titanium (cp Ti) were cast by arc melting, under argon atmosphere, injected by vacuum-pressure. Discs were immersed in artificial saliva and subjected to different temperatures: 37ºC and thermocycling (37ºC/5ºC/37ºC/55ºC/37ºC). After thermocycling, extracts were put in a subconfluent culture during 6 h, and the number of cells and their viability were used to evaluate cytotoxicity in these temperatures. For each alloy, data from temperature conditions were compared by Student's t-test (α=0.05). RESULTS: The cytotoxicity tests with alloy/metal extracts showed that Ni-Cr, Co-Cr-Mo, Ti-6Al-4V and cp Ti extracts (p>0.05) did not affect cell number or cell viability, while Ni-Cr-Ti (p<0.05) extract decreased cell number and viability when the alloy was subjected to thermocycling. CONCLUSION: Within the limitations of the present study, the Ni-Cr-Ti alloy had cell number and viability decreased when subjected to temperature variation, while the other alloys/metal extracts did not show these results.

One of the most important properties of artificial teeth is the abrasion wear resistance, which is determinant in the maintenance of the rehabilitation's occlusal pattern. OBJECTIVES: This in vitro study aims to evaluate the abrasion wear resistance of 7 brands of artificial teeth opposed to two types of antagonists. MATERIAL AND METHODS: Seven groups were prepared with 12 specimens each (BIOLUX & BL, TRILUX & TR, BLUE DENT & BD, BIOCLER & BC, POSTARIS & PO, ORTHOSIT & OR, GNATHOSTAR & GN), opposed to metallic (M & nickel-chromium alloy), and to composite antagonists (C & Solidex indirect composite). A mechanical loading device was used (240 cycles/min, 4 Hz speed, 10 mm antagonist course). Initial and final contours of each specimen were registered with aid of a profile projector (20x magnification). The linear difference between the two profiles was measured and the registered values were subjected to ANOVA and Tukey's test. RESULTS: Regarding the antagonists, only OR (M = 10.45 ± 1.42 µm and C = 2.77 ± 0.69 µm) and BC (M = 6.70 ± 1.37 µm and C = 4.48 ± 0.80 µm) presented statistically significant differences (p < 0.05). Best results were obtained with PO (C = 2.33 ± 0.91 µm and M = 1.78 ± 0.42 µm), followed by BL (C = 3.70 ± 1.32 µm and M = 3.70 ± 0.61 µm), statistically similar for both antagonists (p>0.05). Greater result variance was obtained with OR, which presented the worse results opposed to Ni-Cr (10.45 ± 1.42 µm), and results similar to the best ones against composite (2.77 ± 0.69 µm). CONCLUSIONS: Within the limitations of this study, it may be concluded that the antagonist material is a factor of major importance to be considered in the choice of the artificial teeth to be used in the prosthesis.

Este estudo avaliou o efeito de soluções para enxaguatório bucal contendo fluoreto sobre a superfície do titânio comercialmente puro (cp Ti) após fundição odontológica. As amostras (n=50) foram divididas igualmente: grupo A - armazenadas em água destilada a 37 ± 1ºC, grupo B - armazenadas em água destilada a 37 ± 1ºC e imersão diária em NaF a 0,05% durante 3 min, grupo C - armazenadas em água destilada a 37 ± 1ºC e imersão diária em NaF a 0,2% durante 3 min, grupo D - armazenadas em água destilada a 37 ± 1ºC e imersão em NaF a 0,05% a cada 15 dias por 3 min e grupo E - armazenadas em água destilada a 37 ± 1ºC e imersão em NaF a 0,2% a cada 15 dias durante 3 min. A rugosidade superficial foi medida logo após o polimento metalográfico das amostras (T0) e cada 15 dias de experiência até serem alcançados 60 dias (T15, T30, T45, T60). Os dados foram analisados usando ANOVA (α=0,05) e as diferenças não foram estatisticamente significantes (p>0,05) entre as diferentes soluções. Conclui-se que soluções contendo fluoreto (pH 7,0) não danificam a superfície do Ti cp e podem ser usadas como soluções para bochecho usadas por pacientes que possuem restaurações à base de titânio.

This study evaluated the effects of fluoride-containing solutions on the surface of commercially pure titanium (CP Ti) obtained by casting. CP Ti specimens were fabricated and randomly assigned to 5 groups (n=10): group 1: stored in distilled water at 37 ± 1ºC; group 2: stored in distilled water at 37 ± 1ºC and daily immersed in 0.05% NaF for 3 min; group 3: stored in distilled water at 37 ± 1ºC and daily immersed in 0.2% NaF for 3 min; group 4: stored in distilled water at 37 ± 1ºC; and immersed in 0.05% NaF every 15 days for 3 min; and group 5: stored in distilled water at 37 ± 1ºC and immersed in 0.2% NaF every 15 days for 3 min. Surface roughness was measured with a profilometer immediately after metallographic polishing of the specimens (T0) and at 15-day intervals until completing 60 days of experiment (T15, T30, T45, T60). Data were analyzed statistically by ANOVA and Tukey's test (α=0.05). There was no statistically significant difference (p>0.05) in surface roughness among the solutions. In conclusion, fluoride-containing solutions (pH 7.0) used as mouthwashes do not damage the surface of cast CP Ti and can be used by patients with titanium-based restorations.

Several impression materials are available in the Brazilian marketplace to be used in oral rehabilitation. The aim of this study was to compare the accuracy of different impression materials used for fixed partial dentures following the manufacturers' instructions. A master model representing a partially edentulous mandibular right hemi-arch segment whose teeth were prepared to receive full crowns was used. Custom trays were prepared with auto-polymerizing acrylic resin and impressions were performed with a dental surveyor, standardizing the path of insertion and removal of the tray. Alginate and elastomeric materials were used and stone casts were obtained after the impressions. For the silicones, impression techniques were also compared. To determine the impression materials' accuracy, digital photographs of the master model and of the stone casts were taken and the discrepancies between them were measured. The data were subjected to analysis of variance and Duncan's complementary test. Polyether and addition silicone following the single-phase technique were statistically different from alginate, condensation silicone and addition silicone following the double-mix technique (p < .05), presenting smaller discrepancies. However, condensation silicone was similar (p > .05) to alginate and addition silicone following the double-mix technique, but different from polysulfide. The results led to the conclusion that different impression materials and techniques influenced the stone casts' accuracy in a way that polyether, polysulfide and addition silicone following the single-phase technique were more accurate than the other materials.

Este estudo avaliou o efeito de tratamentos de superfície químico e mecânico para ligas metálicas fundidas sobre a resistência de união de uma resina composta indireta (Artglass) ao titânio comercialmente puro (Ti cp). Trinta varetas cilíndricas metálicas (3 mm diâmetro x 60 mm comprimento) foram fundidas em Ti cp grau 1 e igualmente divididas em grupos de acordo com os seguintes tratamentos de superfície: jateamento, químico, mecânico com esferas de 0,4 mm, mecânico com esferas de 0,6 mm, químico/mecânico com esferas de 0,4 mm e químico/mecânico com esferas de 0,6 mm. Anéis de Artglass (6 mm diâmetro X 2 mm espessura) foram fotopolimerizados ao redor das varetas, de acordo com as recomendações do fabricante. Os corpos-de-prova foram embutidos em gesso-pedra e a resistência de união (MPa) foi medida em uma máquina universal de ensaios com velocidade de 2,0 mm/min e célula de carga de 500 kgf. Os dados foram analisados estatisticamente por ANOVA a um critério e teste de Tukey (a=5%). Houve diferença estatisticamente significante (p<0,05) entre os tratamentos de superfície quanto à resistência adesiva. Retenção química e jateamento apresentaram resultados estatisticamente semelhantes (p=0,139), e ambos apresentaram menores valores de retenção que os demais tratamentos (p<0,05). Em conclusão, a retenção mecânica, associada ou não a tratamento químico, apresentou melhores resultados de resistência adesiva do compósito indireto ao Ti cp.

This study evaluated the effect of chemical and mechanical surface treatments for cast metal alloys on the bond strength of an indirect composite resin (Artglass) to commercially pure titanium (cpTi). Thirty cylindrical metal rods (3 mm diameter x 60 mm long) were cast in grade-1 cpTi and randomly assigned to 6 groups (n=5) according to the received surface treatment: sandblasting; chemical treatment; mechanical treatment - 0.4 mm beads; mechanical treatment - 0.6 mm beads; chemical/mechanical treatment - 0.4 mm; and chemical/mechanical treatment - 0.6 mm beads. Artglass rings (6.0 mm diameter x 2.0 mm thick) were light cured around the cpTi rods, according manufacturer's specifications. The specimens were invested in hard gypsum and their bond strength (in MPa) to the rods was measured at fracture with a universal testing machine at a crosshead speed of 2.0 mm/min and 500 kgf load cell. Data were analyzed statistically by one-way ANOVA and Tukey test (a=5%). The surface treatments differed significantly from each other (p<0.05) regarding the recorded bond strengths. Chemical retention and sandblasting showed statistically similar results to each other (p=0.139) and both had significantly lower bond strengths (p<0.05) than the other treatments. In conclusion, mechanical retention, either associated or not to chemical treatment, provided higher bond strength of the indirect composite resin to cpTi.